The data behind the mix.

Lab blends, dose response, a ready-mix field pour and precast trials. Controls and Trident cylinders are shown together.

+16–31%28-day gain across lab blends

+40%28-day field-pour gain

+159%at 8 hours, precast

Tested by a 3rd party gov't accredited laboratory, Material TEC (AASHTO R18), SGS TEC and Ideal Laboratory.

Strength explorer

Choose a published blend and compare untreated with Trident at 1.2 L/m³ (≈31 fl oz/yd³).

Blend

Dose

Compare standard mix

Explorer20% cement / 80% slag · strength vs age

Trident: design strengthUntreated: design strength

Trident at 1.2 L/m³

20% cement / 80% slag, 31% stronger at 28 days.
Age	Untreated	Trident
3 d	3,118 PSI	4,104 PSI
7 d	3,596 PSI	5,177 PSI
28 d	5,133 PSI	6,699 PSI

3rd party gov't accredited laboratory · M30 · Oct 2026.

+31%28-day gain

101%7-day ÷ untreated 28-day

-65%binder CO₂e vs equal-strength standard 80/20

Fig. 1 · All blends

M30 mixes tested by a 3rd party gov't accredited laboratory. Compressive strength at 3, 7 and 28 days; Trident dosed at 1.2 L/m³ for the treated series.

Blend	3 d control → Trident	7 d control → Trident	28 d control → Trident	28 d gain	Trident 7 d ÷ control 28 d
75% cement / 25% fly ash	3,364 → 4,698	4,031 → 5,003	5,597 → 6,511	+16%	89%
50/50 fly ash	3,292 → 4,031	3,857 → 5,177	5,264 → 6,510	+24%	98%
50/50 slag	3,408 → 4,887	4,060 → 5,423	5,307 → 6,728	+27%	102%
40% cement / 60% slag	3,451 → 4,336	3,886 → 5,307	5,177 → 6,192	+20%	103%
30% cement / 70% slag	3,103 → 4,278	4,089 → 5,409	5,264 → 6,453	+23%	103%
20% cement / 80% slag	3,118 → 4,104	3,596 → 5,177	5,133 → 6,699	+31%	101%

Fig. 2 · 80% slag dose response

Fig. 220% cement / 80% slag · dose response

20% cement / 80% slag

80 percent slag dose response at 7 and 28 days.
Dose, mL/m³	Dose, fl oz/yd³	7-day strength	28-day strength
0	0	3,596 PSI	5,133 PSI
600	15.4	3,973 PSI	5,525 PSI
800	20.5	4,582 PSI	6,003 PSI
1000	25.6	4,872 PSI	6,322 PSI
1200	30.7	5,177 PSI	6,699 PSI

3rd party gov't accredited laboratory · M30 · Oct 2026.

Fig. 3 · Field pour

Fig. 350% slag · strength vs age

Trident: design strengthUntreated: design strength

1 week instead of 4.

The field mix reached untreated 28-day strength at 7 days and finished 40% higher.
Age	Untreated	Trident
1 d	1,220 PSI	1,470 PSI
7 d	4,350 PSI	7,030 PSI
14 d	5,540 PSI	8,990 PSI
28 d	7,090 PSI	9,940 PSI

Producer QC lab · ASTM C39 · poured control · breaks Jul 30–Aug 26, 2026.

Fig. 5 · Precast plant trials

5AMix 201 · early strength

1 turn

3 turns

Pour 7:15 AM · strip 3:15 PM, same shift

+1,709 PSI · +159% · 2,786 PSI vs 1,077 PSI

Later ages: 28-day 8,362 PSI → 9,396 PSI (+12%).

With Trident, Mix 201 reached the producer's release requirement at 8 hours, taking the plant from one mold turn a day to three. The release-strength value was not provided.
Hours	Untreated	Trident
8 h	1,077 PSI	2,786 PSI
10 h	3,102 PSI	4,292 PSI
12 h	3,980 PSI	4,704 PSI
24 h	6,875 PSI	7,598 PSI

North American precast producer · ASTM C39 · cumulative cylinder averages.

5BBatch 3 · 24-hour clock

Batch 3 measurements only.

Batch 3 only: Trident measured 3,800 PSI at 12 hours. Untreated measured 2,870 PSI at 14 hours. The customer specification was 3,500 PSI at 24 hours.
Batch 3 result	Age	Strength
Trident	12 hours	3,800 PSI
Untreated	14 hours	2,870 PSI
Customer specification	24 hours	3,500 PSI

Batch 3 only. Customer specification: 3,500 psi at 24 hours.

Age	Control	Trident	Gain
8 hours	1,077 psi	2,786 psi	+159%
10 hours	3,102 psi	4,292 psi	+38%
12 hours	3,980 psi	4,704 psi	+18%
24 hours	6,875 psi	7,598 psi	+11%
7 days	7,487 psi	8,186 psi	+9%
14 days	8,394 psi	8,836 psi	+5%
28 days	8,362 psi	9,396 psi	+12%